PET CSD BOTTLES


TLE-102 WATER BOTTLE GRADE

SPECIFICATION:TLE-102
FEATURE AND PERFORMANCE:Comparing with TLE-102, it has more favorable barrier property and higher resistance against stress and cracking.
APPLICABILITY:Soda water bottle, soda pop bottle 3gal., 5gal. large bottle.
MAIN RAW MATERIAL:PTA, MEG, IPA



Features And Performance:

Comparing with Dragon PET TLE-102, it has more favorable barrier property and higher resistance against stress and cracking.

Applicability:

Soda water bottle, soda pop bottle 3gal., 5gal. large bottle.

Main Raw Material:

PTA, MEG, IPA

Dragon PET TLE-102 bottle level polyester chip is applicable for producing various soda pop bottles and 3gal., 5gal. large bottles.

This product has features of low heavy metal content, low aldehydes content, favorable color value, stable viscosity and favorable processability. Because unique process formula and production techniques are used, and the process control and quality control are reinforced, this brand of new product has outstanding barrier property to prevent CO2 leakage, it is resistant against stress and crack, and has low process temperature and wide process range, the product bottle has a favorable transparency and high final product acceptance rate, and can effectively protect the soda pop bottle from cracking under stress during the quality assurance period.

We have complete production techniques and devices imported from US Dupont and Switzerland Bühler. Production and management conform to ISO9001 quality system, the Dragon PET bottle level polyester chip has stable and reliable quality, and we have won a lot of trust from the clients.

Detailed Specifications “Dragon” Brand “TLE-102” Bottle-grade Polyester Chips

ITEMUNITINDEXTEST METHOD
I.V.dL/g0.85±0.02ASTM D4603-03
AAppm≤1.0GC
DEG%1.25±0.2GC
M.P.249±2DSC
COOHmmol/kg≤35Titration
  COLORL VALUE≥80GB17931-2003
B VALUE≤0GB17931-2003
CRYSTALIZATION%≥45DSC
HUMIDITY%≤0.4IR
IMPURITIESgranula /500gNULLGB17931-2003
ASH%≤0.08GB17931-2003
DUSTmg/kg≤100GB17931-2003